HIGH PURITY POROUS CORDIERITE CERAMIC

POROUS CORDIERITE CERAMIC DISC

HIGH PURITY POROUS CORDIERITE CERAMIC 
Made from the high purity mineral Mg2Al4Si5O18 which is also 2MgO·2Al2O3·5SiO2, a magnesium alumino-silicate. 












This material is an extremely lightweight material with low thermal expansion and excellent strength, rigidity and thermal shock resistance; and has very good corrosion resistance to chemicals at high temperature, and high use temperature. It may be used for a variety of electrical, mechanical, and thermal applications

The specifications for these components are as follows:
Outside Diameter: Approximately 3.470” +/- 0.010" (90.4 mm)
Thickness: Approximately 0.100" +/- 0.005"  (2.5 mm)
Specific Gravity or Density:   2.6 g/cm3
Water Absorption or Gas Permeability -- Porosity: ~50%
Fusion Temperature or Melting Temperature:   1450 °C or 2642 °F
Maximum Working Temperature:   1200 °C or 2200 °F
Thermal Conductivity:  0.3 W/m* K
Expansion Coefficient or CTE from RT-600°C:  3 x 10-6 inches/°C
Electrical Resistivity at 20 C:   1014 Ohm*cm
Electrical resistance at 600 C:  10Ohm*cm
Modulus of Elasticity:   14 x 106 p.s.i. or 250 GPa.
Dielectric Constant @ 6 GHz: Approximately 6.4 @RT
Dielectric Loss @ 6 GHz: Approximately 0.0005 @RT